Liquid Silicone Rubber Takes the Heat

LSR is also approved for medical applications where it will be in contact with skin. Its stability prevents it from affecting skin or, in turn, being affected by skin contact. Some grades of LSR, when combined with the appropriate manufacturing environment can be used in implantable applications. Its hydrophobic (water-repellent) properties make it ideal for water-handling applications. And the fact that it is fire-retardant and does not emit toxins or halogens when burned suits it well for a variety of safety applications. Reviewing material specifications or consulting your moulder for more details is generally recommended.

Thermoplastics vs. Thermosets

In some aspects of the way they are moulded, thermoplastics—polyethylene, polypropylene, polycarbonate and ABS, among others—and thermosets like LSR are opposites. Thermoplastics start out solid at room temperature, soften when heated, and re-solidify when cooled, which makes them excellent candidates for recycling. Thermosets, on the contrary, typically start out as gels and solidify permanently when heated with a platinum catalyst. That makes them poor candidates for recycling but accounts for their superior performance at high temperatures.

These differences in their response to heat define their respective moulding processes. Thermoplastic pellets are heated before injection to liquefy the resin and then allowed to cool in the mould before being ejected. Thermosetting resin, on the other hand, is chilled before injection and then heated in the mould for curing.

Shear Thinning

Before curing, liquid silicone rubber is a shear thinning fluid, also called a pseudoplastic. Shear thinning is the reduction of a fluid’s viscosity when shear stress (like that caused by injection into a mould) is applied, and it significantly impacts the way LSR behaves in the mould. To understand the behaviour of a pseudoplastic material, consider ketchup, which, like LSR, is a sheer thinning fluid, as compared to honey, which is not.

Think about what happens when you tip a bottle of ketchup. Then picture tipping that little plastic bear full of honey. At room temperature the honey will flow, albeit slowly; the ketchup probably won’t because the ketchup is more viscous. That’s why you end up shaking the ketchup bottle or fishing down the neck with a table knife. Now imagine the ketchup in a squeeze bottle, and squeeze that and the plastic honey dispenser side by side. The honey is difficult to dispense while the ketchup flows freely, taking mere seconds to cover your burger or fries. This change in viscosity is an example of shear thinning, and the same thing happens to LSR when it is injected into a mould. Shear thinning has both positive and negative effects on the moulding of LSR. It actually improves flow through thin-walled areas, reducing the need to maintain uniform wall thickness throughout a part as is recommended when moulding thermoplastics. On the other hand, because LSR flows so easily in a mould, it has an increased tendency to flash — to seep into spaces where mould halves meet — creating unwanted vestiges that must be removed by secondary operations (see Figure 3). Flash can be prevented or at least minimized through careful mould design but is still a factor in part design.

Parts moulded of LSR will continue to shrink after being removed from the mould as they cool. This is partly due to the typically higher mould temperature. For this reason, they do not cling to cores as thermoplastics do; instead they tend to stick to the mould half with the greatest surface area. Because of the material’s flexibility, different parts of a finished piece may stick to each mould half leaving the part hanging after the mould opens. Preventing this problem may require some redesign of the part.

Design Considerations for LSR Parts

From the part designer’s standpoint, design guidelines for LSR are similar to those for thermoplastic though somewhat more relaxed in certain areas. The reason for the relaxation is that LSR, being flexible, is a more forgiving material than thermoplastics. Planes that are parallel to the direction of mould opening typically require some draft to allow milling of the mould, though not to prevent scraping of the part against the mould wall during ejection. About one degree per inch of mould depth is usually sufficient.

Because shear-thinning LSR flows easily in the mould, it can traverse thin walls that would cause fill problems for thermoplastics. For the same reason, uniform wall thickness is not as critical. And because thermoset material is solidified by heat and is mostly cured before it cools, sink is not a problem, which means that part features can be made thicker than with typical thermoplastic material (although there are still good reasons not to make features thicker than they need to be). But the biggest difference between thermoplastic and thermoset LSR mould design may be in the handling of undercuts.

Rigid thermoplastics can be moulded with undercuts either by the use of side-actions that produce the undercut features and then withdraw before the mould opens to allow the part to be ejected, or by complicated techniques like pickouts. But because LSR is so flexible, finished parts can often be “peeled” out of the mould. This means that features that, moulded in thermoplastic, would be trapped behind an undercut to be pulled around the projection. The only real constraint on undercuts in LSR is whether they can be milled.

LSR Moulding at Protolabs

As it has for thermoplastics, Protolabs’ automated design analysis, also supports LSR. The process for submitting a design for production in LSR is similar to that for thermoplastics.

• Upload the design.
• Specify the material and quantity.
• Get a firm quote with design analysis and pricing information, typically within hours.

Current turnaround time for LSR production is three weeks. For some designs, faster turnaround may be available with an expedite fee. This is far faster than is possible using traditional methods because the Protolabs process turns 3D CAD models directly into toolpaths for milling moulds. As with thermoplastics, the process for making LSR moulds at Protolabs is managed using proprietary software running on a very large compute cluster. The toolpaths generated by the software run automatic milling machines that produce the mould halves, which are then placed into specialized liquid silicone moulding presses.

The process can cost-effectively produce LSR parts in quantities from 25 to 5,000+. In moderate production quantities, the process can turn out parts faster and less expensively than traditional LSR moulding processes, but even at very small production or prototyping volumes, Protolabs still uses full-scale manufacturing processes. This is significantly different from other LSR prototyping operations.

Most producers of low-volume LSR prototypes hand mix the component gels in a blender, a process that cannot match the process control of Protolabs’ industrial process. In some cases, they don’t use a milled mould or heat-cured LSR. Instead, the prototypes are made using a room temperature vulcanization process that starts with a thermoplastic copy of the part made on a 3D printer. A mould is cast around the 3D-printed part and hand-filled using a caulking gun. The resulting part may be suitable for testing form and fit, but since it does not duplicate the manufacturing process or use real LSR material, it cannot be relied on for functional testing or actual production at any volume.

To get real parts for prototyping, traditional producers have often had to wait until manufacturing moulds have been made, which can take weeks or months. At this late stage of development, problems that show up can cause serious setbacks in the development process and the scrapping of very expensive tools. Protolabs’ automated aluminium mould milling allows cost-effective prototyping using real materials and industrial processes earlier in development when redesign is easier, less time consuming and less costly.

Protolabs is continually expanding its processes and capabilities. Its current requirements and design considerations are listed.

• Maximum part size is 304mm x 203mm x 100mm.* This is the size envelope that -the part must be able to fit in, although the part cannot occupy that full space. *Part sizes may increase with the expansion of capability.
• The part’s maximum projected mould area must not exceed 31,200mm². Note that this is smaller than the full 61,712mm² footprint of a part that would fully occupy the 304mm by 203mm dimensions mentioned above. The reason for this limitation is that the pressure exerted in filling a mould with a mould area greater than 31,200 mm² would exceed the clamp pressure of the moulding press.
• Maximum part volume is 217,000mm³. This is determined by the maximum shot volume of Protolabs’ current LSR moulding equipment.
• Wall thickness can be as thin as 0.5mm. The issue is not ability to fill, but ability to mill thinner walls and to remove the thinner-walled parts from the mould without damage.
• Due to LSR’s shear thinning, variation in wall thickness is generally not a problem.
• Rib thickness should be from 0.5 to 1.0 times the thickness of the adjoining wall.
• The radius of inside fillets should be approximately equal to the wall thickness.
• Sink is almost non-existent, but elimination of unnecessarily thick areas will reduce material cost.
• To eliminate flash, parting lines should be kept as simple and short as possible.
• Removal of LSR from the mould is typically done manually rather than by ejector pins. The part should be designed to be retained entirely in one mould half, and some feature of the part should rise above the parting line surface to facilitate hand removal.
• Many parts with simple undercuts can be easily removed from the mould by the press operator without mechanical assistance. Parts with undercuts will be reviewed on a case-by-case basis for feasibility.
• LSR parts generally require draft similar to that of thermoplastics, approximately one degree of draft per inch (25.4mm.) of depth. Zero draft may be tolerated on shallow parts. LSR is more tolerant of reduced draft than thermoplastics. This will be determined on a case-by-case basis.
• Due to LSR’s easy flow, it requires relatively small gates for resin injection. Gates should ideally feed into the thickest or broadest cross-section of the part, though this is not an absolute requirement. LSR edge gates will leave a vestige or blemish and should be placed on a surface that is not dimensionally or cosmetically critical or in a recess.
• Protolabs will, if necessary, add vents, overflows or tear strips to improve part quality. These may leave a small vestige on the finished part. Protolabs will propose gate and vent locations, which customers must approve, before manufacturing the tool.
• Protolabs offers the following finishes on LSR moulding tools:
  • PM-F0
  • PM-F1
  • SPI-C1
  • PM-T1
  • PM-T2
  • SPI-A2
• More finishes will be added in the near future, and special requests will be given consideration.
• Typical tolerances for a well-designed part are linear tolerances of 0.025mm/mm.

Protolabs also offers a number of secondary moulds and tooling services to support your project.

-